Bifunctional nanoporous ruthenium-nickel alloy nanowire electrocatalysts towards oxygen/hydrogen evolution reaction

A class of ruthenium-nickel alloy catalysts featured with nanoporous nanowires (NPNWs) were synthesized by a strategy combining rapid solidification with two-step dealloying. RuNi NPNWs exhibit excellent electrocatalytic activity and stability for oxygen evolution reaction (OER) and hydrogen evolution reaction (HER) in which the RuNi-2500 NPNWs catalyst shows an OER overpotential of 327 mV to deliver a current density of 10 mA cm^?2 and the RuNi-0 NPNWs catalyst requires the overpotential of 69 mV at 10 mA cm^?2 showing the best HER activity in alkaline media. Moreover, the RuNi-1500 NPNWs catalyst was used as the bifunctional electrocatalyst in a two-electrode alkaline electrolyzer for water splitting, which exhibits a low cell voltage of 1.553 V and a long-term stability of 24 h at 10 mA cm^?2, demonstrating that the RuNi NPNWs catalysts can be considered as promising bifunctional alkaline electrocatalysts.     

NiFe layered double hydroxide as an efficient bifunctional catalyst for electrosynthesis of hydrogen peroxide and oxygen

Two electron oxygen reduction reaction to produce hydrogen peroxide (H₂O₂) is a promising alternative technique to the multistep and high energy consumption anthraquinone process. Herein, Ni–Fe layered double hydroxide (NiFe-LDH) has been firstly demonstrated as an efficient bifunctional catalyst to prepare H₂O₂ by electrochemical oxygen reduction (2e^? ORR) and oxygen evolution reaction (OER). Significantly, the NiFe-LDH catalyst possesses a high faraday efficiency of 88.75% for H₂O₂ preparation in alkaline media. Moreover, the NiFe-LDH catalyst exhibits excellent OER electrocatalytic property with small overpotential of 210 mV at 10 mA cm^?2 and high stability in 1 M KOH solution. On this basis, a new reactor has been designed to electrolyze oxygen and generate hydrogen peroxide. Under the ultra-low cell voltage of 1 V, the H₂O₂ yield reaches to 47.62 mmol g_cat^?1 h^?1. In order to evaluate the application potential of the bifunctional NiFe-LDH catalyst for H₂O₂ preparation, a 1.5 V dry battery has been used as the power supply, and the output of H₂O₂ reaches to 83.90 mmol g_cat^?1 h^?1. The excellent electrocatalytic properties of 2e^? ORR and OER make NiFe-LDH a promising bifunctional electrocatalyst for future commercialization. Moreover, the well-designed 2e^? ORR-OER reactor provides a new strategy for portable production of H₂O₂.     

Fabrication of CuO/MoO3 p-n heterojunction for enhanced dyes degradation and hydrogen production from water splitting

The development of excellent photocatalytic material is highly required for energy and environmental applications. In this study, visible light responsive p-n heterojunction photocatalysts based on CuO/MoO₃ with varying ratios of CuO were prepared by the facile hydrothermal method. The crystalline structure, surface morphology, chemical compositions and optical properties of the synthesized photocatalysts were studied using X-ray powder diffraction (XRD), scanning electron microscopy (SEM), Energy-dispersive X-ray spectroscopy (EDX), X-ray photoelectron spectroscopy (XPS), Fourier-transform infrared spectroscopy (FTIR), photoluminescence (PL) techniques and UV–Vi's absorption spectroscopy. The results showed that the 5%CuO/MoO₃ nanocomposite displayed enhanced photocatalytic performance for the production of hydrogen (98.5 μmol h^?1g^?1) and degradation of dyes rhodamine B (RhB) and alizarine yellow (AY) than all other samples. Furthermore, 5% CuO/MoO₃ composite exhibited excellent stability after five consecutive cycles for both RhB and AY dyes. Overall, the improved photocatalytic performance of 5%CuO/MoO₃ composite was due to increased adsorption of visible light, good surface morphology, enhanced charge separation/transfer which inhibited recombination of electrons and holes. This study could encourage the synthesis of novel and effective p-n heterojunction photocatalysts for practical applications.     

Amorphous-crystalline cobalt-molybdenum bimetallic phosphide heterostructured nanosheets as Janus electrocatalyst for efficient water splitting

Efficient and sustainable Janus catalysts toward hydrogen evolution reaction (HER) and oxygen evolution reaction (OER) are highly desirable for future hydrogen production via water electrolysis. Herein we report an active Janus electrocatalyst of amorphous-crystalline cobalt-molybdenum bimetallic phosphide heterostructured nanosheets on nickel foam (CoMoP/CoP/NF) for efficient electrolysis of alkaline water. As-reported CoMoP/CoP/NF consists of amorphous bimetal phosphide nanosheets doped with crystalline CoMoP/CoP heterostructured nanoparticles on NF. It can efficiently catalyze both HER (η = 127 mV@100 mA cm^?2) and OER (η = 308 mV@100 mA cm^?2) in alkaline electrolyte with long-term durability. Serving as anode and cathode of water electrolyzer, CoMoP/CoP/NF generates electrolytic current of 10, 50 and 100 mA cm^?2 at low voltage of 1.50, 1.59, and 1.67 V, respectively.     

Rare earth metals co-doped ZnO/CNTs composite as high performance photocatalyst for hydrogen production from water_triethanolmine mixture

This study investigated the zinc oxide (ZnO) based heterojunction photocatalysts for improved hydrogen production from water splitting. A sol-gel route was adopted to produce terbium (Tb) and samarium (Sm) co-doped ZnO/CNTs composites where CNTs worked as a support material. The built-in redox couples of lanthanides in co-doped TS-ZnO/CNTs composite showed higher hydrogen evolution activity than Sm doped (Sm-ZnO/CNTs) and Tb doped (Tb–ZnO/CNTs) photocatalysts. When triethanolamine was utilized as a sacrificial agent, the TS-ZnO/CNTs photocatalyst result in a remarkable hydrogen evolution rate of 2683 molh^?1g^?1 under visible light illumination. The optimum photocatalyst also showed high stability over five successive hydrogen evolution cycles. The better hydrogen evolution rate with TS-ZnO/CNTs was referred to its fine particle size, high reactive surface area, small optical band gap, suppressed reunification of charge carriers and built-in redox couples. The photocatalytic mechanism, involved in water splitting with TS-ZnO/CNTs photocatalyst, is also deduced in this study. This study can stimulate the attempts towards construction of lanthanides based co-doped semiconductor photocatalysts for efficient hydrogen evolution.     

Zeolitic-imidazolate frameworks-derived Co3S4/NiS@Ni foam heterostructure as highly efficient electrocatalyst for oxygen evolution reaction

Transition metals sulfide-based nanomaterials have recently received significant attention as a promising cathode electrode for the oxygen evolution reaction (OER) due to their easily tunable electronic, chemical, and physical properties. However, the poor electrical conductivity of metal-sulfide materials impedes their practical application in energy devices. Herein, firstly nano-sized crystals of cobalt-based zeolitic-imidazolate framework (Co-ZIF) arrays were fabricated on nickel-form (NF) as the sacrificial template by a facile solution method to enhance the electrical conductivity of the electrocatalyst. Then, the Co₃S₄/NiS@NF heterostructured arrays were synthesized by a simple hydrothermal route. The Co-ZIFs derived Co₃S₄ nanosheets are grown successfully on NiS nanorods during the hydrothermal sulfurization process. The bimetallic sulfide-based Co₃S₄/NiS@NF-12 electrocatalyst demonstrated a very low overpotential of 119 mV at 10 mA cm^?2 for OER, which is much lower than that of mono-metal sulfide NiS@NF (201 mV) and ruthenium-oxide (RuO₂) on NF (440 mV) electrocatalysts. Furthermore, the Co₃S₄/NiS@NF-12 electrocatalyst showed high stability during cyclic voltammetry and chronoamperometry measurements. This research work offers an effective strategy for fabricating high-performance non-precious OER electrocatalysts.     

Synergistic regulation of hydrogen adsorption/desorption via dual interfaces of Cu/Ni/Ni(OH)2 toward efficient hydrogen evolution reaction

Nickel-based catalysts have attracted tremendous attention as alternatives to precious metal-based catalysts for electrocatalytic hydrogen evolution reaction (HER) in virtue of their conspicuous advantages such as abundant reserves and high electrochemical activity. Nevertheless, a great challenge for Ni-based electrocatalyst is that nickel sites possess too strong adsorption for key intermediates H1, which severely suppresses the hydrogen-production activities. Herein, we report a hierarchical architecture Cu/Ni/Ni(OH)₂ consisting of dual interfaces as a high-efficient electrocatalyst for HER. The Cu nanowire backbone could provide geometric spaces for loading plenty of Ni sites and the formed Ni/Cu interface could effectively weakened the adsorption intensity of H1 intermediates on the catalyst surface. Moreover, the H1 adsorption could be further controlled to appropriate states by in-situ formed Ni(OH)₂/Ni interface, which simultaneously promotes water adsorption and activation, thus both Heyrovsky and Volmer steps in HER could be obviously accelerated. Experimental and theoretical results confirm that this interface structure can promote water dissociation and optimize H1 adsorption. Consequently, the Cu/Ni/Ni(OH)₂ electrocatalyst exhibits a low overpotential of 20 mV at 10 mA cm^?2 and an ultralow Tafel slope of 30 mV dec^?1 in 1.0 M KOH, surpassing those of reported transition-metal-based electrocatalysts and even the prevailing commercial Pt/C.     

Structure engineering of amorphous P–CoS hollow electrocatalysts for promoted oxygen evolution reaction

Oxygen evolution reaction (OER) is a key process involved in many energy-related conversion systems. An ideal OER electrocatalyst should possess rich active sites and optimal binding strength with oxygen-containing intermediates. Although numerous endeavors have been devoted to the modification and optimization of transition-metal-based OER electrocatalysts, they are still operated with sluggish kinetics. Herein, an ion-exchange approach is proposed to realize the structure engineering of amorphous P–CoS hollow nanomaterials by utilizing the ZIF-67 nanocubes as the precursors. The precise structure control of the amorphous hollow nanostructure contributes to the large exposure of surface active sites. Moreover, the introduction of phosphorus greatly modifies the electronic structure of CoS₂, which is thus favorable for optimizing the binding energies of oxygenated species. Furthermore, the incorporation of phosphorus may also induce the formation of surface defects to regulate the local electronic structure and surface environment. As a result of this, such P–CoS hollow nanocatalysts display remarkable electrocatalytic activity and durability towards OER, which require an overpotential of 283 mV to afford a current density of 10 mA cm^?2, outperforming commercial RuO₂ catalyst.     

S/Se dual-doping promotes the formation of active Ni/Fe oxyhydroxide for oxygen evolution reaction of (sea)water splitting

Surface reconstruction produces metal oxyhydroxide (1OOH) active sites, and promoting surface reconstruction is essential for the design of OER electrocatalysts. In this paper, we reported that a large amount of active NiFeOOH was generated in-situ on the surface of nickel-iron sulfide selenide, thus exposing more active sites and efficiently catalyzing OER. In 1 M KOH solution, NiFeOOH(S,Se) achieves an ultra-low overpotential of 195 mV at the current density of 10 mA cm^?2, and the Tafel slope is only 31.99 mV dec^?1, showing excellent catalytic performance. When the current density is 100  mA cm^?2, the over-potential of NiFeOOH(S,Se) in KOH + seawater solution is 239 mV, which is almost equivalent to 231 mV in KOH solution. The excellent OER stability of the NiFeOOH(S,Se) catalyst in alkaline electrolytes was confirmed, and the overpotential did not change significantly after 4 days of testing in KOH + seawater solution.     

Anodic corrosion of heteroatom doped graphene oxide supports and its influence on the electrocatalytic oxygen evolution reaction

Transition metal-based electrocatalysts supported on carbon substrates face the challenges of anodic corrosion of carbon during oxygen evolution reaction at high oxidation potential. The role of electrophilic functional groups (carbonyl, pyridinic, thiol, etc.) incorporated in graphene oxide has been studied towards the anodic corrosion resistance. Heteroatom functionalized carbon supports possess modified electronic properties, surface oxygen content, and hydrophilicity, which are crucial in governing electrochemical corrosion in the alkaline oxidative environment. Evidently, electron-withdrawing groups in NGO support (pyridinic, cyano, nitro, etc) and its lower oxygen content impart maximum corrosion resistance and anodic stability in comparison to the other sulfur-doped and co-doped graphene oxide support. In this report, we establish the baseline evaluation of carbon-supported OER electrocatalysts by a systematic analysis of activity and substrate corrosion resistance. The result of this study establishes the role of surface composition of the doped supports while for designing a stable, corrosion-resistant OER electrocatalyst.